7 Kinds Common Bending Methods You Should Know About Metal Press Brake

Existem muitas maneiras para a dobradeira CNC dobrar chapas, e existem muitos métodos de classificação para diferentes princípios. Este artigo apresenta especificamente vários métodos comuns de dobra das diferentes posições relativas dos moldes superior e inferior e as diferentes formas dobradas durante a dobra, e detalha as processo de dobra e precauções.

A Posição Relativa de Flexão de Metal Press Brake Ferramental

First of all, according to the difference in the relative positions of the upper and lower molds during the bending process, the bending process is divided into two forms: gap bending and bottom pressing. The characteristics and differences between the two are as follows: Metal Press Brake

• Curvatura de espaço

The CNC press brake is not pressed between the upper die and the lower die during the bending process. The required bending angle is obtained by adjusting the depth of the upper die entering the opening of the lower die. This bending method is called gap bending. Metal Press Brake

The deeper the upper die enters the lower die, the smaller the bending angle; otherwise, the larger it is. Due to the elasticity of the material, it is also necessary to consider excessive bending to control the amount of spring-back when bending. Metal Press Brake

The advantage of gap bending is that a smaller number of molds can be used to realize forming processing of various angles, and the required processing pressure is small. Usually, in order to obtain the best bending effect, the ratio of the thickness B of the material to the width V of the V-shaped opening of the lower die can be selected as follows: Metal Press Brake

1. Quando a espessura do material é inferior a 12,7 mm, B: V é 1:8;
2. Quando a espessura do material é 12,7 ~ 22,2 mm, B: V é 1:10;
3. Quando a espessura do material é superior a 22,2 mm, B:V é 1:12.

The above three ratios are standard mold ratios, the material is low carbon steel, and the material strength is 43.4kg/mm2. When compiling a bending processing program, the above parameters can be set in the numerical control system, and the processing program will be generated by the system after automatic processing. Metal Press Brake

• Dobra inferior

When the CNC press brake adopts the bottom bending, the plate is pressed between the upper and lower dies, so as to obtain the required bending angle and elbow radius. CNC bending machine press bottom bending is suitable for processing metal sheets with a thickness of less than 2mm in batch and large-scale production in enterprises. Metal Press Brake

Seu raio de dobra é pequeno, a precisão de dobra é alta e a precisão é boa. Deve-se notar que a pressão de trabalho da prensagem inferior é maior do que a da flexão de folga, geralmente mais de três vezes.

O ângulo da matriz de prensagem inferior deve ser adaptado ao ângulo da placa e ao material. Normalmente, ao dobrar aço de baixo carbono na parte inferior, o ângulo dos moldes superior e inferior deve ser consistente com o ângulo necessário da chapa. Quando o método de prensagem inferior é usado para processamento, a relação da matriz, ou seja, a relação entre a espessura da folha B e a distância de abertura V da matriz inferior é B:V = 1:6.

During the bending process to determine the working tonnage, the force between the upper and lower dies is applied to the material, causing the material to plastically deform. Working tonnage refers to the bending pressure during bending. The influencing factors for determining the working tonnage are bending radius, bending method, mold ratio, elbow length, thickness and strength of bending material, etc. Metal Press Brake

De acordo com as diferentes formas formadas após a dobra, o processo de dobra é dividido em dobra em L, dobra em N, dobra em Z, dobra e achatamento reverso, hardware de prensagem e outras formas.

Tipo de dobra diferente

• L Dobra

De acordo com o ângulo, é dividido em dobra de 90° e não dobra de 90°. O processamento é dividido em processamento geral (L>V/2).

O molde é selecionado de acordo com o material, espessura da placa e ângulo de conformação.

Relying on the principle: Metal Press Brake

1. Com base no princípio de duas posições pós-fixadas e posicionamento de acordo com a forma da peça de trabalho.
2. Quando o medidor traseiro da máquina dobradeira CNC estiver em posição, preste atenção à deflexão, e é necessário que esteja no mesmo centro que o tamanho da dobra da peça.
3. Quando pequenas curvas são feitas, é melhor processá-las na posição inversa.
4. É melhor estar na parte de trás e mais baixo no meio. (O medidor traseiro não é fácil de levantar quando está em posição).
5. It is better to be close to the rear set. Metal Press Brake
6. It is better to lean on the long side. Metal Press Brake
7. Use um gabarito para auxiliar no posicionamento (posicionamento irregular da hipotenusa).

Matters needing attention: Pay attention to the positioning method during processing and the movement mode specified in the various positioning processing methods. The mold is bent when it is installed, and then it is required to be pulled back to prevent the workpiece from being deformed during bending. Metal Press Brake

When a large workpiece is internally bent, because the workpiece has a large shape and a small bending area, it is difficult for the tool and the bending area to overlap, resulting in difficult positioning of the workpiece or damage to the bending workpiece.

In order to avoid the above situation, a positioning point can be added in the longitudinal direction of the processing, so that the positioning and processing are carried out in two directions, which makes the processing and positioning convenient, and improves the processing safety, avoids the damage of the workpiece, and improves the production efficiency.

• N Dobra

N dobras requerem diferentes métodos de processamento de acordo com diferentes formas. Ao dobrar, o lado interno do material deve ser maior que 4 mm e o tamanho da dimensão X é limitado pela forma do molde. Se o lado interno do material for inferior a 4 mm, métodos especiais são usados para processamento.

A seleção da matriz é baseada na espessura do material, tamanho, material e ângulo de dobra.

Princípio de confiança: certifique-se de que a peça de trabalho não interfere com a ferramenta

1. Certifique-se de que o ângulo de reclinação seja ligeiramente inferior a 90 graus.
2. É melhor usar duas posições pós-fixadas, exceto em casos especiais.

Precauções:

Depois de dobrar a dobra em L, o ângulo deve ser garantido em 90 graus ou ligeiramente inferior a 90 graus para facilitar o processamento e o posicionamento.

Quando a segunda dobra é processada, é necessário que a posição de localização esteja centralizada na superfície de processamento.

• Dobra Z

A dobra em Z da máquina de dobradeira CNC também é chamada de diferença de passo, ou seja, uma dobra positiva e uma negativa. De acordo com o ângulo, pode ser dividido em hipotenusa e borda reta. O tamanho mínimo do processo de dobra é limitado pela matriz de processamento e o tamanho máximo de processamento é determinado pela forma da máquina de processamento. Em circunstâncias normais, quando o lado interno do material dobrado em Z for menor que 3,5T, o processamento diferencial da matriz é usado. Quando é maior que 3.5T, o método de processamento normal é adotado.

Baseando-se no princípio:

1. É conveniente confiar e tem boa estabilidade.
2. Geralmente, a posição é a mesma que a dobra em L.

A posição secundária é exigir que a peça de trabalho fique plana com a matriz inferior.

Precauções:

1. O ângulo de processamento da dobra em L deve estar no lugar, geralmente 89,5~90 graus.
2. Quando este último precisar ser puxado para trás, preste atenção à deformação da peça de trabalho.
3. A ordem de processamento deve estar correta.
4. Para processamento especial, os seguintes métodos podem ser usados: método de separação de linha central (processamento excêntrico), processamento em V pequeno (necessidade de aumentar o coeficiente de dobra), fácil formação de molde e moagem de molde inferior.

• Achatamento Reflexo

A dobra e o achatamento reverso também são chamados de prensagem de borda morta. As etapas de processamento da borda morta são: a primeira dobre e insira a uma profundidade de cerca de 35 graus e, em seguida, use uma matriz de achatamento para achatá-la até que fique plana e apertada.

1. Método de seleção da matriz: de acordo com 5 a 6 vezes a espessura do material, selecione a largura da ranhura em V da matriz inferior com uma profundidade de 30 graus e selecione a matriz superior de acordo com as condições específicas de processamento de bordas mortas.
2. Assuntos que precisam de atenção: Preste atenção ao paralelismo dos dois lados da borda morta. Quando o tamanho de processamento da borda morta é longo, a borda achatada pode ser dobrada primeiro e depois achatada. Para bordas mortas mais curtas, pode-se usar dunnage.

• Hardware de prensa

O uso de uma dobradeira para prensar e segurar peças de ferragens geralmente requer o uso de moldes auxiliares, como moldes côncavos e gabaritos. Em geral, existem porcas de pressão, pinos de pressão, parafusos de pressão e algumas outras peças.

Precauções:

1. Quando a forma da peça de trabalho precisa ser evitada para processamento, ela deve ser evitada.
2. Após o processamento, é necessário verificar o torque, se o empuxo atinge o padrão e se as ferragens e a peça de trabalho estão planas e firmes.
3. Ao prensar após a dobra, ao prensar além da máquina-ferramenta, preste atenção para evitar a usinagem e o paralelismo do molde.
4. Se for uma expansão, deve-se notar também que não deve haver rachaduras na borda da expansão, e a borda da expansão não deve ser mais alta que a superfície da peça de trabalho.

Tempo estimado de leitura: 9 minutos